Thermoplastic Vibration manufacturers of hazard warning tap forroad marking1.ISOcertified factory direct offer
2.adhesion
Thermoplastic Vibration manufacturers of hazardwarning tap for road marking ---
Specification:
Has the features of resistance excellent compression resistance and after molding & curing,when the wheel press the line will emergeproper frequency vibration and plangent, has a good safety warning effect, in the rainy night, the protuberance portion can produce the reflected light so that it can provide an audible warning on high speed roads; a proven safety measure to inform motorists and pedestrians or serve as noise generators when run across a road, or attempt to wake a sleeping driver when installed in the shoulders of a road.
Application Scope:
The highway turns, highway lane edge line,tunnel centerline used as the dividing line,
city bus line used as the dividing line, ramp, toll plaza, ramp export transverse reduction
line, city road intersection stop line, special traffic lane line etc.
Test Report of Vibration Thermoplastic Road MarkingPaint
Density /g/cm3 | 1.95 |
Softening Point/°C | 116 |
Color and appearance of coating film | After drying , no wrinkle, spot , falling off, sticking to the wheel .And the color and shape of coating has not large differences to standard plate |
Cure time /minutes | 3 |
Chromaticity Coordinates/(x,y) | X:0.322 Y:0.342 |
Compressive Strength/Mpa | 13.9 -- 23°C±1°C 2.4 -- 50°C±2°C |
Luminance Factor | 0.80 |
Content of glass beads(%) | 22.9 |
Anti-watering | No abnormal phenomenon dunking in water for 24h |
Anti-alkali | No abnormal phenomenon dunking in calcium hydroxide saturated solution for 24h |
Low temperature Anti-cracking of coating layer | Keep 4h in -10°C ,and lay 4h in normal temperature as a circulation .And continuously do three circulations , no crack |
Heating stability | Keep 4h in 200~220°C in agitating condition, no obviously yellowing, burnt , blocked |
Test Report of Reflective Thermoplastic Road MarkingPaint
Density /g/cm3 | 2.02 |
SofteningPoint/°C | 103 |
Color and appearance of coating film | After drying , no wrinkle, spot , falling off, sticking to thewheel .And the color and shape of coating has not large differencesto standard plate |
Cure time /minutes | 3 |
Chromaticity Coordinates/(x,y) | X:0.318 Y:0.337 |
CompressiveStrength/Mpa | 15.4 |
Luminance Factor | 0.80 |
AbrasionPerformance/mg(200r/1000greduce weight) | 55.2 |
Content of glass beads(%) | 22.6 |
Flow resistance | 39 |
Low temperature Anti-cracking of coating layer | Keep 4h in -10°C , and lay 4h in normal temperature as acirculation .And continuously do three circulations , nocrack |
Heating stability | Keep 4h in 200~220°Cin agitating condition, no obviouslyyellowing, burnt , blocked |
Test Report of Thermoplastic Road MarkingPaint
Density /g/cm3 | 1.95 |
Viscosity | 139 |
Color and appearance of coating film | After drying , no wrinkle, spot , falling off, sticking to thewheel .And the color and shape of coating has not large differencesto standard plate |
Cure time /minutes | 10 |
Cover Rate(%) | 98 |
Chromaticity Coordinates/(x,y) | X:0.311 Y:0.328 |
CompressiveStrength/Mpa | 13.9 -- 23°C±1°C 2.4 -- 50°C±2°C |
Luminance Factor | 0.83 |
AbrasionPerformance/mg(200r/1000greduce weight) | 21.5 |
Anti-watering | No abnormal phenomenon dunking in water for 24h |
Anti-alkali | No abnormal phenomenon dunking in calcium hydroxide saturatedsolution for 24h |
Flexibility/mm | 1 |
SolidContent/% | 71.2 |